SBS Modified Bitumen Elastomeric Waterproofing roll on Membrane

SBS Modified Bitumen Waterproofing Membrane is made using SBS (styrene-butadiene-styrene) thermoplastic elastomer-modified asphalt as the coating material. The carrier can be high-quality polyester mat, fiberglass mat, or glass-reinforced polyester mat. The surfacing materials include fine sand, mineral granules, PE film, and aluminum film. The membrane is produced through specialized mechanical mixing and milling.

Width:1000mm Thickness:3mm/4mm Exceptional Low Temperature Flexibility PY/G/PYG PE/S/M/ Polyester /Glass Fiber Reinforcemen Torch Applied Heat Fusion Seams

Whatsapp

SBS modified bitumen membrane

Specifications

Carrier types: polyester (PY), fiberglass (G), and glass-reinforced polyester (PYG).
Upper surface release material: PE film, fine sand (S), or mineral granules (M). Lower surface release material: fine sand (S) or PE film.
Mechanical properties: Type I and Type II.
Standard width: 1000 mm.

Applications

Roofing waterproofing for industrial, commercial, and residential buildings.
Below-grade waterproofing and damp-proofing for industrial and residential buildings, including indoor swimming pools and fire water tanks.
Civil engineering projects: subways, tunnels, bridge decks with concrete paving, wastewater treatment plants, and landfills.
Water conservancy facilities: canals and reservoirs.

Product Features

Long-fiber polyester mat membranes:

Combines high-performance long-fiber polyester mat with SBS modified bitumen – an excellent all- around membrane.
Forms a high-strength waterproof layer with strong resistance to water pressure.
High tensile strength and elongation – adapts well to substrate shrinkage, deformation, and cracking.
Excellent high and low temperature resistance – suitable for both hot and cold climates, especially cold regions.
High-strength polyester mat offers strong puncture, tear, and fatigue resistance.
Good resistance to corrosion, mold, and weathering.
Easy torch application year-round – hot-air welded seams are reliable and durable.

Alkali-free fiberglass mat membranes:

Combines an economical carrier with high-performance SBS modified bitumen.
High tensile strength and excellent high/low temperature resistance.
Resistant to corrosion, mold, and weathering – easy to install.

Glass-reinforced polyester mat membranes:

Can be installed using mechanical fastening – safe and environmentally friendly.
Offers better dimensional stability.

SBS bitumen membrane Performance

Elastomer/plastic modified asphalt waterproofing membrane complies with GB18242-2008 standard.

No .	Parameter		Index
			Ⅰ		Ⅱ
			PY	G	PY	G	PYG
		3mm	2100				–
		4mm	2900				–
1	Soluble content （g/m 2 ）	5mm	3500
		Test phenomenon	–	Carrier non- combustible	–	Carrier non- combustible	–
2	Heat resistance	℃	90		105
		≤ mm	2
		Test phenomenon	No flow, no drip
3	Low temperature flexibility℃		-20		-25
4	Water impermeability (30min)		0 . 3 Mpa	0 . 2 Mpa	0 . 3 Mpa
5	Tensile strength	Max peak (N/50mm) ≥	500	350	800	500	900
		Secondary peak (N/50mm) ≥	–	–	–	–	800
		Test phenomenon	During stretching, partial cracking of asphalt coating or separation from carrier occurs on some specimens
6	Elongation	At max peak (％ ) ≥	30	–	40		–
		At secondary peak(％ ) ≥	–		–		15
7	Mas s increase after waterimmersion ( ％) ≤	PE 、 S	1.0
		M	2 .0
		Tensile retention (％ ) ≥	90
		Elongation retention (％ ) ≥	80
8	Heat aging	Low temperature flexibility (℃)	– 1 5		-20
			no cracks
		Dimensional change (％ ) ≤	0 .7	–	0 .7	–	0 .3
		M a s s l o s s (％ ) ≤	1.0
9	Oil migration	Sh e et s ≤	2 .0
10	Peel strength of joint (N/mm) ≥		1.5
11	Nail tear strength a（N） ≥		–				300
12	Mineral granule adhesion b（g） ≤		2 .0
13	Lower asphalt coating thickness c(mm) ≥		1.0
14	Accelerated weathering	Appearance	no slip , flow , drip
		Tensile retention (％ ) ≥	80
		Low temperature flexibility (℃ )	– 1 5		-20
			no cracks
a Only for membranes used in single-layer mechanical fastening.b Only for mineral-surfaced membranes.c Only for torch-applied membranes.